Уплыў перадавых тэхналогій на тэрмін службы цепластойлівай сталі

The characteristics of the morphology and distribution of inclusions, grain thickness and brittle phase, and the role of chemical composition, metamorphic treatment, heat treatment and metal pouring of ZG0Cr23Ni13 heat-resistant steel were studied. After complex tests, data statistics and comparison, it can be concluded that compound metamorphism treatment, metal pouring, solid treatment and Раставанне вакууму і іншыя перадавыя тэхналогіі адрозніваюцца для паляпшэння механічных уласцівасцей пакаёвай тэмпературы, высокай тэмпературнай і цеплааддачы, што тлумачыцца ўдакладненне movement. In the analysis of casting failure, there are many factors leading to failure, mainly thermal fatigue leading to crack germination and development. Correspondingly, there are a series of factors that affect the initiation and expansion of the cracks, among which, the sulfur content is extremely important, because the cracks mostly develop along the sulfide. If the Змест серы ўплывае на сыравіну і якасць іх плаўкі, калі кастынг, якія працуюць пад ахоўнай атмасферай вадароду, серавадародны сера ў вадародзе прывядзе да таго, каб кідка прасякнуць серу . па -другое, адэкватнасць цвёрдага лячэння рашэнняў паўплывае на моцную жорсткасць лініі ліцця .