Працэс SHAW; Працэс кашыцы MO (U)

Спосаб вытворчасці, выраблены з керамічнай пасты . керамічная завісь, выраблена з этылавага сілікату гідралізату і тонкага рефрактерного пяску з чыстай тэкстурай і высокай цеплавой устойлівасці, напрыклад, электрычнай лава -кварца, цыркона, колеру, і г.д. as the catalyst. Because of the ingredients used and its appearance are similar, so it is called the ceramic type. Ceramic casting is a new process developed on the ordinary basis. There are two types of ceramic type: ① ceramic type is all made by ceramic grouting. The production process is the first fixed on the plate, the coat sand box, and then the adjusted ceramic slurry into the sand box, to harden the mold, after high temperature roasting is to become cast.② Using the bushing, in the gap between the bushing and the appearance of the ceramic slurry for casting. Bushing can be used in sand type, but also available. Irrigation of ceramic shell with bushing can save a lot of ceramic slurry and can be used more in production. Ceramic castings can reach Ra 10 ~ 1.25 microns, up to 3~5 levels, can achieve the purpose. Ceramic casting has a short production cycle and a high metal utilization rate. The largest casting can reach more than ten tons, mainly used for casting large thick wall Дакладнае ліццё і ліццё адзінай невялікай партыі штампоўкі, коўкі, пластыкавай формы, ліцця штампаў, шкляной цвілі і іншых формаў . Тэрмін службы керамічнай формы ліцця супастаўная з формай, вырабленай метадам, у той час як кошт вытворчасці ніжэй, чым зроблены метадам апрацоўкі.