1.1 Зваранасць цеплавой сталі малібдэна з малібдэна
Chromium and molybdenum are the main alloy elements, pearlite heat-resistant steel significantly improve the high temperature strength and high temperature oxidation resistance of metals, but they make metal welding performance, welding seam and heat affected zone in which has a high tendency, quenching in air cooling after welding is easy to produce the hard and brittle martensite structure, not only affects the mechanical properties of welded joint, and produce a lot of stress, Thus Тэндэнцыя халоднай расколіны .
Такім чынам, галоўнай праблемай цеплааддачанай зваркі з'яўляюцца расколіны, а ўтварэнне расколін - гэта тры элементы: структура, стрэс і ўтрыманне вадароду ў зварцы, таму асабліва важна распрацаваць разумны працэс зваркі .}
2.1 канаўка
Groove processing is usually done by flame or plasma cutting process. When necessary, cutting should also be preheated, and PT inspection should be done after polishing to remove the cracks on the groove. Usually choose v-type groove, groove Angle is 60℃, from the point of view of preventing crack, groove Angle is more favorable, but increase the welding amount, and the groove and inside both Бакі зямлі чыстыя, выдаліце алей, іржа і вада і іншы бруд (гідрарод, прадухіляе сітаватасць) .
2.2 Усталюйце
Запыт не можа прымяняць групу, каб прадухіліць унутранае напружанне, з -за высокай тэндэнцыі расколін малібдэна з малібдэна з малібдэна, таму, калі шва зваркі ступені абмежавання не занадта вялікі, публічны нумар WeChat: кароль звар
2.3 Выбар метаду зваркі
У цяперашні час звычайна выкарыстоўваюцца метады зваркі для зваркі трубаправода ў нафтавых і нафтахімічных устаноўках - гэта GTAW для ніжняй і электроднай дугі для вечка . Іншыя метады зваркі ўключаюць міг зваркі, зваркі CO2, зварачны зваркі электраслэга і аўтаматычную запчастак дузе і г.д. {2}
2.4 Выбар зварачных матэрыялаў
The principle of selecting welding materials, the alloy composition and strength performance of weld metal should be basically consistent with the corresponding index of the base metal or should reach the lowest performance index proposed by the technical conditions of the product. And in order to reduce the hydrogen content should be with alkaline low hydrogen type electrode, electrode or flux should be in accordance with the provisions, drying technology, along with it, WeChat public number: micro welder, put them in electrode increases with the increasing use in heat insulation barrels, electrode to no more than 4 hours in the heat insulation barrels, otherwise should resume drying, drying times shall not be more than three times, in the process of concrete construction, have detailed provisions. Austenitic stainless steel electrode, such as A307, can also be used for manual arc welding of Цеплавая сталь Chromium-molybdenum, але яе ўсё ж трэба папярэдне разагрэць перад зваркай . Гэты метад падыходзіць для сітуацыі, каб зваркі не могуць быць апрацаваны цяпла пасля зваркі .}
2,5 Разагрэў
Разагрэў з'яўляецца важнай тэхналагічнай мерай для халоднай расколіны і вывядзення стрэсу ў зварцы перилита цепластойлівай сталі ., каб забяспечыць якасць зваркі, разагрэў і падтрыманне пэўнага тэмпературнага дыяпазону павінна ажыццяўляцца як у працэсе фіксацыі і зваркі .}}}}
2.6 Павольнае астуджэнне пасля зваркі
Пасля зваркі павольнае астуджэнне - гэта прынцып зваркі малібдэн -рэзістэнтнай сталі малібдэна, якая павінна быць строга, нават у гарачае лета трэба зрабіць гэта, як правіла, адразу пасля зваркі з азбеставай тканінай, якая ахоплівае зваркі і каля зоны шва, невялікія зварачныя кавалачкі можна размясціць у азбестнай тканіне павольнае астуджэнне .}}}}
2,7 пасля садавіны тэрмічная апрацоўка
Цеплавая апрацоўка павінна ажыццяўляцца адразу пасля зваркі, каб прадухіліць затрымку парэпання, выключыць стрэс і палепшыць мікраструктуру .